Item |
ASTM |
Unit: SI
(conventional) |
P-1001A |
P-3001S |
Mechanical
Properties |
Density |
D-792 |
- |
1.21 |
1.21 |
| Water absorption (1/8", 24hrs) |
D-570 |
% |
0.26 |
0.24 |
| Light transmittance (Thickness: 3mm) |
D-1003 |
% |
88 |
89 |
| Tensile strength |
D-638 |
MPa {kg/cm2}
|
69 {700} |
66 |
| Elongation at break |
D-638 |
% |
50 |
45 |
| Bending strength |
D-790 |
MPa {kg/cm2} |
81 {830} |
84 |
| Bending modulus |
D-790 |
GPa {kg/cm2} |
2.1 {21,000} |
2.2 |
| Compressive strength (Yield) |
D-695 |
MPa {kg/cm2} |
81 {830} |
- |
| Izod impact strength (1/8", with notch) |
D-256 |
J/m
{kg-Ecm/cm} |
196 {20} |
300 |
| Rockwell hardness |
D-785 |
R |
123 |
- |
Thermal
properties
|
Deflection temperature under load
1.8MPa {18.6kg/cm2} |
D-648 |
°C |
175 |
169 |
| Linear expansion coefficient |
D-696 |
10-5/K
{10-5cm/cm/°C} |
6.2 |
6.0 |
Electrical
Properties |
Dielectric breakdown strength |
D-149
|
MV/m {kv/mm} |
31 |
|
| Specific volume resistivity |
D-257 |
Ωm {Ωcm} |
2x1014
{2x1016} |
|
| Dielectric constant (106Hz) |
D-150 |
PF/m |
27 {3.0} |
|
| Dielectric dissipation factor(106Hz) |
D-150 |
- |
0.01 |
|
| Ark resistance |
D-495 |
s |
127 |
|
| Tracking resistance |
IEC |
V |
- |
|
Other
properties |
Molding shrinkage (Thickness: 3mm)
Flow direction, orthogonal direction |
- |
% |
0.8 |
0.8 |