U polymer
P series resins composite grade
(1) L-1003PA
Characteristics
- Heat resistance, creep resistance, and excellent lubricant
Properties
|
ASTM |
Unit: SI (conventional) |
L-1003PA |
|
Mechanical Properties |
Density | D-792 |
- |
1.23 |
Water absorption (1/8", 24hrs) | D-570 |
% |
0.26 |
|
Light transmittance (Thickness: 3mm) | D-1003 |
% |
- |
|
Tensile strength | D-638 |
MPa {kg/cm2} |
70 |
|
Elongation at break | D-638 |
% |
60 |
|
Flexural strength | D-790 |
MPa {kg/cm2} |
82 {840} |
|
Flexural modulus | D-790 |
GPa {kg/cm2} |
2.2 |
|
Compressive strength (Yield) | D-695 |
MPa {kg/cm2} |
- |
|
Izod impact strength (1/8", with notch) |
D-256 |
J/m {kg-Ecm/cm} |
280 |
|
Rockwell hardness | D-785 |
R |
123 |
|
Thermal properties |
Deflection temperature under load 1.8MPa {18.6kg/cm2} |
D-648 | °C |
175 |
Coefficient of linear thermal expansion | D-696 |
10-5/K {10-5cm/cm/°C} |
6.2 |
|
Electrical Properties |
Dielectric breakdown strength | D-149
|
MV/m {kv/mm} |
31 |
Specific volume resistivity | D-257 |
Ωm {Ωcm} |
2x1014 {2x1016} |
|
Dielectric constant (106Hz) | D-150 |
PF/m |
27 |
|
Dielectric dissipation factor(106Hz) | D-150 |
- |
0.01 |
|
Ark resistance | D-495 |
s |
127 |
|
Tracking resistance | IEC |
V |
- |
|
Other properties |
Molding shrinkage (Thickness: 3mm) Flow direction, orthogonal direction |
- |
% |
0.8 |
Technical Data
Properties of lubricant materials
|
|
|
1.8MPa {18.6kg/cm2} |
|
|
kPa • m/s {kg/cm2 • cm/s} |
{954} |
{383} |
|
|
|
{mm3/km • kg} |
|
|
|
◎ |
Δ |
|
◎ |
Ο |
|
Ο |
Ο |
|
Δ |
◎ |
*Counterpart: S45C ◎: Excellent Ο: Good, Δ: inferior
(2) PT-3020
Characteristics
- Dimensional accuracy (planarity)
- Heat resistance
- Creep resistance and elasticity
- Rigidity
Properties
|
ASTM |
Unit: SI (conventional) |
PT-3020 |
|
Mechanical Properties |
Density | D-792 |
- |
1.36 |
Water absorption (1/8", 24hrs) | D-570 |
% |
0.12 |
|
Light transmittance (Thickness: 3mm) | D-1003 |
% |
- |
|
Tensile strength | D-638 |
MPa {kg/cm2} |
67 |
|
Elongation at break | D-638 |
% |
6 |
|
Flexural strength | D-790 |
MPa {kg/cm2} |
111 |
|
Flexural modulus | D-790 |
GPa {kg/cm2} |
3.8 |
|
Compressive strength (Yield) | D-695 |
MPa {kg/cm2} |
- |
|
Izod impact strength (1/8", with notch) |
D-256 |
J/m {kg-Ecm/cm} |
60 |
|
Rockwell hardness | D-785 |
R |
- |
|
Thermal properties |
Deflection temperature under load 1.8MPa {18.6kg/cm2} |
D-648 | °C |
165 |
Coefficient of linear thermal expansion | D-696 |
10-5/K {10-5cm/cm/°C} |
3.5~4.0/3.8~4.3 |
|
Electrical Properties |
Dielectric breakdown strength | D-149
|
MV/m {kv/mm} |
- |
Specific volume resistivity | D-257 |
Ωm {Ωcm} |
- |
|
Dielectric constant (106Hz) | D-150 |
PF/m |
- |
|
Dielectric dissipation factor(106Hz) | D-150 |
- |
- |
|
Ark resistance | D-495 |
s |
- |
|
Tracking resistance | IEC |
V |
- |
|
Other properties |
Molding shrinkage (Thickness: 3mm) Flow direction, orthogonal direction |
- |
% |
0.3~0.4/0.4~0.5 |
(3) C300VN
Characteristics
- Flame resistant, transparent (flame resistance: UL94 V-0, 0.8 mmt)
- High flow
Properties
|
ASTM
|
Unit: SI (conventional) |
C300VN |
|
Mechanical Properties |
Density | D-792 |
- |
1.29 |
Water absorption (1/8", 24hrs) | D-570 |
% |
0.24 |
|
Light transmittance (Thickness: 3mm) | D-1003 |
% |
- |
|
Tensile strength | D-638 |
MPa {kg/cm2} |
75 |
|
Elongation at break | D-638 |
% |
40 |
|
Flexural strength | D-790 |
MPa {kg/cm2} |
95 |
|
Flexural modulus | D-790 |
GPa {kg/cm2} |
2.5 |
|
Compressive strength (Yield) | D-695 |
MPa {kg/cm2} |
- |
|
Izod impact strength (1/8", with notch) |
D-256 |
J/m {kg-Ecm/cm} |
65 |
|
Rockwell hardness | D-785 |
R |
- |
|
Thermal properties |
Deflection temperature under load 1.8MPa {18.6kg/cm2} |
D-648 | °C |
155 |
Coefficient of linear thermal expansion | D-696 |
10-5/K {10-5cm/cm/°C} |
6.5 |
|
Electrical Properties |
Dielectric breakdown strength | D-149
|
MV/m {kv/mm} |
30 |
Specific volume resistivity | D-257 |
Ωm {Ωcm} |
2x1014 {2x1016} |
|
Dielectric constant (106Hz) | D-150 |
PF/m |
26 |
|
Dielectric dissipation factor(106Hz) | D-150 |
- |
0.01 |
|
Ark resistance | D-495 |
s |
125 |
|
Tracking resistance | IEC |
V |
175 |
|
Other properties |
Molding shrinkage (Thickness: 3mm) Flow direction, orthogonal direction |
- |
% |
0.8 |