NylonResin > Nano-Composite Nylon6 > General Properties of Nonocomposite Nylon Series Resins Top Page
[UNITIKA Nylon Resin] Nano-Composite Nylon6

General Properties of Nonocomposite
Nylon Series Resins

Type
Nonocomposite nylon
Mechanical
Properties
Item
Test
condition
Test
method
(ASTM)
Unit: SI
M1030DH
M2350
M1030B
M1030E
When
absolutely
dry
When
wet
When
absolutely
dry
When
wet
When
absolutely
dry
When
wet
When
absolutely
dry
When
wet
Tensile
strength
Yielding
D-638
MPa
               
Breaking
93
62
88
59
85
55
96
65
Tensile
elongation
Yielding
D-638
%
               
Breaking
4
5
5
6
20
35
4
4
Bending
strength
D-790
MPa
158
80
140
72
133
50
155
78
Bending
modulus
D-790
GPa
4.5
2.2
4.0
1.7
3.7
1.5
5.2
2.5
Izod impact
strength
With notch
D-256
J/m
45
127
44
211
40
250
30
70
Rockwell
hardness
R scale
D-785
114
113
90
Shearing
strength
D-732
MPa
62
48
Compressive
strength
D-695
MPa
85
60
Taber
abrasion
CS-17
1kg
D-1044
mg/
1000
rpm
               
Thermal
properties
Linear
expansion
coefficient
D-696
10-5/K
5.3
6.3
4.9
Specific
heat
 
J/(g•K)
Heat
conductivity
C-177
w/(m•K)
Deflection
temperature
under load
1.8MPa
D-648
°C
152
 
147
 
120
 
164
0.45MPa
193
 
193
 
190
 
197
Electrical
Properties
Specific
volume
resistivity
D-257
Ω-m
1x1013
1x1013
1x1013
Dielectric
breakdown
strength
Short-term
D-149
MV/m
27
27
Dielectric
constant
106HZ
D-150
pF/m
35
Dielectric
dissipation
factor
106HZ
D-150
0.019
Ark
resistance
D-495
sec
122
IEC
tracking
IEC112
V
Other
Properties
Density
D-792
1.15
1.15
1.14
1.15
Water
absorption
In water,
23°C,
24 hr
%
0.9
1.0
0.7
Equilibrium
under
50%RH,
23°C
2.8
2.8
2.8
2.8
Molding
shrinkage
(3.2 mm
thickness)
Flow
direction
D-955
%
0.8
0.8
0.8
0.8
Orthogonal
direction
1.0
1.0
1.0
0.9

Value after equilibrium water absorption under 50% RH and 23°C