XecoT™

Properties List

Properties Table List

Standard Grade

Item Test
condition
Test
Method
Units XN400 XG310A30A XG310A50A XG510A30D XG510A50D
Non-
reinforced
GF
reinforced
Good flow
GF
reinforced
Good flow
GF
reinforced
GF
reinforced
Mechanical
Properties
Tensile stress At yield ISO 527-1, -2 MPa 84 144 190 181 223
Tensile strain At break ISO 527-1, -2 % 7 4 4 5 5
Flexural strength ISO 178 MPa 110 238 310 264 344
Flexural modulus ISO 178 MPa 2500 8300 15000 8900 14800
Charpy impact
strength
With notch ISO 179-1eA kJ/m² 5 8 10 10 13
Rockwell hardness R scale ISO 2039 120 120 120 120
Thermal
Properties
DTUL 1.8MPa ISO 75-1, -2 °C 123 302 308 302 310
Electronic
Properties
Dielectric constant 1MHz IEC 60250 3.8
Comparative
tracking Index
IEC 60112 V 600
Flow
Properties
MFR Load 1.2kg ISO 1133 g/10min 30 30 25 7 5
°C 330 340 340 340 340
Other
Properties
Density ISO 1183 g/cm³ 1.14 1.36 1.57 1.36 1.57
Mold shrinkage MD ISO 294-4 % 1.5 0.2 0.2 0.2 0.2
TD 1.5 0.6 0.5 0.6 0.5

Last Updated: 12 February 2015

High function grade

Item Test
condition
Test
Method
Units XV310A30 XI500 XD361A40 XB510A30D
Flame-
resistant
High
Toughness
Precision
molding
CF
reinforced
Mechanical
Properties
Tensile stress At yield ISO 527-1, -2 MPa 150 49 99 227
Tensile strain At break ISO 527-1, -2 % 4 32 3 4
Flexural strength ISO 178 MPa 220 69 165 336
Flexural modulus ISO 178 MPa 11500 1600 9700 19200
Charpy impact
strength
With notch ISO 179-1eA kJ/m² 10 84 2 7
Rockwell hardness R scale ISO 2039
Thermal
Properties
DTUL 1.8MPa ISO 75-1, -2 °C 302 112 278 302
Electronic
Properties
Dielectric constant 1MHz IEC 60250 3.7
Comparative
tracking Index
IEC 60112 V 425
Flow
Properties
MFR Load 1.2kg ISO 1133 g/10min 10 25 9
°C 340 330 340
Flammability UL94   V-0      
Other
Properties
Density ISO 1183 g/cm³ 1.60 1.07 1.49 1.28
Mold shrinkage MD ISO 294-4 % 0.2 1.4 0.4 0.2
TD 0.4 1.4 0.5 0.6

Last Updated: 12 February 2015

LED Reflectors

Item Test
condition
Test
Method
Units XR300A37 XR310A45
High-gloss Standard
Mechanical
Properties
Tensile stress At yield ISO 527-1, -2 MPa 50 95
Tensile strain At break ISO 527-1, -2 % 2 4
Flexural strength ISO 178 MPa 92 150
Flexural modulus ISO 178 MPa 3700 6300
Charpy impact
strength
With notch ISO 179-1eA kJ/m² 2 2
Rockwell hardness R scale ISO 2039
Thermal
Properties
DTUL 0.45MPa ISO 75-1, -2 °C 256 304
Electronic
Properties
Dielectric constant 1MHz IEC 60250
Comparative
tracking Index
IEC 60112 V
Flow
Properties
MFR Load 1.2kg ISO 1133 g/10min
°C
Other
Properties
Density ISO 1183 g/cm³ 1.53 1.59
Mold shrinkage MD ISO 294-4 % 0.7 0.4
TD 1.2 0.5

Last Updated: 12 February 2015