General properties of TERRAMAC resins
Injection grades
Test method |
ISO |
Unit |
Basic grade TE-2000 |
High- impact grade TE-1030 |
High- impact grade TE-1070 |
Heat-resistant grade TE-7003 |
Heat resistance, High-rigidity grade TE-8303 |
Heat resistance, High-rigidity grade TE-8003G30 |
Heat resistance, Impact resistance grade TE-8005M |
Heat resistance, Impact resistance grade TE-8005MT9 |
Heat resistance, Impact resistance grade TE-9005MT9 |
Appearance | - |
- |
Trans parent |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Biomass content |
- |
- |
99.5 |
70 |
30 |
95 |
65 |
65 |
90 |
80 |
80 |
Density | 1183 |
g/cm³ |
1.25 |
1.24 |
1.24 |
1.25 |
1.49 |
1.47 |
1.24 |
1.28 |
1.31 |
Melting point | - |
°C |
170 |
170 |
170 |
170 |
170 |
170 |
170 |
170 |
170 |
Tensile strength |
527 |
MPa |
63 |
51 |
34 |
56 |
54 |
99 |
43 |
41 |
35 |
Tensile elongation |
527 |
% |
4 |
170 |
200< |
3 |
2 |
2 |
31 |
15 |
7 |
Flexural strength |
178 |
MPa |
106 |
77 |
50 |
105 |
102 |
150 |
80 |
77 |
80 |
Flexural modulus |
178 |
GPa |
4.3 |
2.6 |
1.4 |
4.1 |
9.4 |
9.4 |
3.7 |
5.1 |
4.7 |
Charpy impact strength: With notch |
179 |
kJ/m2 |
1.6 |
2.3 |
5.6 |
3.0 |
2.0 |
6.0 |
23 |
11 |
5 |
Deflection temperature under load of 0.45 MPa |
75 |
°C |
58 |
51 |
54 |
108 |
145 |
163 |
100 |
122 |
146 |
Molding shrinkage | - |
% |
0.3~0.5 |
0.3~0.5 |
0.3~0.5 |
0.9~1.1 |
0.3~0.5 |
0.1~0.3 |
0.9~1.0 |
0.6~0.8 |
0.6~0.8 |
Last Updated: 6 December 2017
* The data above are typical values of test pieces determined by our tests, and are not intended to guarantee the properties of resins in a particular application.
Injection grades, Alloy
Test method |
ISO |
Unit |
High-durability grade TDA-8070M |
High-durability grade TAA-8070 |
High-durability, flame-resisting grade TCA-8070MN |
Appearance | - |
- |
Opaque white |
Transparent |
Opaque white |
Biomass content |
- |
% |
30 |
30 |
30 |
Density | 1183 |
g/cm³ |
1.10 |
1.21 |
1.21 |
Tensile strength |
527 |
MPa |
39 |
74 |
51 |
Tensile elongation |
527 |
% |
12 |
8 |
68 |
Flexural strength |
178 |
MPa |
62 |
116 |
80 |
Flexural modulus |
178 |
GPa |
2.2 |
3.6 |
2.6 |
Charpy impact strength: With notch |
179 |
kJ/m2 |
42 |
2 |
12 |
Deflection temperature under load of 0.45 MPa |
75 |
°C |
82 |
72 |
88 |
Molding shrinkage | - |
% |
0.3~0.5 |
0.3~0.5 |
0.3~0.5 |
Flammability | UL-94 |
- |
- |
- |
V-2 (1.6,2.5mm) |
Last Updated: 6 December 2017
* The data above are typical values of test pieces determined by our tests, and are not intended to guarantee the properties of resins in a particular application.
Extrusion, blow, and foam sheet grades
Test method |
ISO |
Unit |
Basic grade TP-4000 |
Soft TP-4030 |
Soft TP-5040 |
Soft CPR-JI |
Foam HV-6250H |
Appearance | - |
- |
Tran sparent |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Density | 1183 |
g/cm³ |
1.25 |
1.24 |
1.32 |
1.35 |
1.27 |
Melting point | - |
°C |
170 |
170 |
165 |
165 |
170 |
Tensile strength |
527 |
MPa |
66 |
50 |
25 |
25 |
69 |
Tensile elongation |
527 |
% |
5 |
44 |
3.4 |
>100 |
2 |
Flexural strength |
178 |
MPa |
108 |
71 |
44 |
40 |
111 |
Flexural modulus |
178 |
GPa |
4.6 |
2.4 |
2.1 |
1.6 |
4.7 |
Charpy impact strength: With notch |
179 |
kJ/m2 |
1.6 |
2.6 |
50 |
>30 |
1.9 |
Deflection temperature under load of 0.45 MPa |
75 |
°C |
59 |
52 |
49 |
55 |
120*1 |
Molding shrinkage | 190°C 2.16kg |
g/10min |
3~5 |
3~5 |
7~10 |
3~5 |
1~3 |
Last Updated: 6 December 2017
* The data above are typical values of test pieces determined by our tests, and are not intended to guarantee the properties of resins in a particular application.
*1 This data is a temperature shown in molding at a predetermined die temperature(110°C).
In molding with a die of a lower temperature, the temperature is approx. 60°C.