RESIN
Grade List
Application | Grade | Characteristics | Applications | BPS positive list No. |
Injection | TE-2000 | Standard, transparent | Smaller goods, containers, various plastic parts, etc. |
C00395 |
TE-1030 | High-impact | C00316 | ||
TE-1070 | Flexible and high-flow | C00316 | ||
TE-7000 | High heat resistance, low density |
Containers, table wear, chassis, etc. |
C00292 | |
TE-7307 | High heat resistance, high-rigidity |
C00292 | ||
TE-7300 | High heat resistance, high-rigidity |
C00292 | ||
TE-8210 | High heat resistance, durability, high-rigidity |
C00317 | ||
TE-8300 | High heat resistance, durability, high-rigidity |
C00317 | ||
Extrusion, blow, and foam |
TP-4000 | Improved melt properties | Containers, bottles, pipes, Foam sheet, etc. |
C00315 |
TP-4030 | Improved melt properties, high-impact |
C00315 | ||
HV-6250H | Improved melt properties | C00319 |
Properties
Injection grades
Item Test method |
ISO | Unit | Basic grade TE-2000 |
High- impact grade TE-1030 |
High- impact grade TE-1070 |
Heat- resisting grade TE-7000 |
Heat- resisting grade TE-7307 |
Heat- resisting grade TE-7300 |
High- durability grade TE-8210 |
High- durability grade TE-8300 |
Appearance | - | - | Tran sparent |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Opaque white |
Density | 1183 | - | 1.25 | 1.24 | 1.24 | 1.27 | 1.42 | 1.47 | 1.42 | 1.47 |
Melting point | - | °C | 170 | 170 | 170 | 170 | 170 | 170 | 170 | 170 |
Breaking strength |
527 | MPa | 63 | 51 | 34 | 70 | 54> | 54 | 50 | 56 |
Tensile elongation |
527 | % | 4 | 170 | 200< | 2 | 2 | 1 | 2 | 1 |
Bending strength |
178 | MPa | 106 | 77 | 50 | 110 | 85 | 98 | 90 | 104 |
Bending modulus |
178 | GPa | 4.3 | 2.6 | 1.4 | 4.6 | 7.5 | 9.5 | 6.8 | 9.3 |
Charpy impact strength: With notch |
179 | kJ/m² | 1.6 | 2.3 | 5.6 | 2.0 | 2.5 | 2.4 | 4.0 | 2.8 |
Deflection temperature under load of 0.45 MPa |
75 | °C | 58 | 51 | 54 | 110 | 120 | 140 | 120 | 140 |
Molding shrinkage | - | % | 0.3∼0.5 |
0.3∼0.5 | 0.3∼0.5 | 1.0∼1.2 | 1.0∼1.2 | 1.0∼1.2 | 1.0∼1.2 | 1.0∼1.2 |
* The data above are typical values of test pieces determined by our tests,
and are not intended to guarantee the properties of resins in a particular application.
Extrusion, blow, and foam sheet grades
Item Test method |
ISO | Unit | Basic grade TP-4000 |
Soft TP-4030 |
Foam HV-6250H |
Appearance | - | - | Tran sparent |
Opaque white |
Opaque white |
Density | 1183 | - | 1.25 | 1.24 | 1.27 |
Melting point | - | °C | 170 | 170 | 170 |
Breaking strength |
527 | MPa | 66 | 50 | 69 |
Tensile elongation |
527 | % | 5 | 44 | 2 |
Bending strength |
178 | MPa | 108 | 71 | 111 |
Bending modulus |
178 | GPa | 4.6 | 2.4 | 4.7 |
Charpy impact strength: With notch |
179 | kJ/m² | 1.6 | 2.6 | 1.9 |
Deflection temperature under load of 0.45 MPa |
75 | °C | 59 | 52 | 120*1 |
Molding shrinkage | 190°C 2.16kg |
g/10min | 3∼5 | 3∼5 | 1∼3 |
* The data above are typical values of test pieces determined by our tests,
and are not intended to guarantee the properties of resins in a particular application.
*1 This data is a temperature shown in molding at a predetermined die temperature(110°C).
In molding with a die of a lower temperature, the temperature is approx. 60°C.